Photodetectors operating across the near‐ to short‐wave infrared (NIR–SWIR,λ= 0.9–1.8 µm) underpin modern science, technology, and society. Organic photodiodes (OPDs) based on bulk‐heterojunction (BHJ) active layers overcome critical manufacturing and operating drawbacks inherent to crystalline inorganic semiconductors, offering the potential for low‐cost, uncooled, mechanically compliant, and ubiquitous infrared technologies. A constraining feature of these narrow bandgap materials systems is the high noise current under an applied bias, resulting in specific detectivities (D^*, the figure of merit for detector sensitivity) that are too low for practical utilization. Here, this study demonstrates that incorporating wide‐bandgap insulating polymers within the BHJ suppresses noise by diluting the transport and trapping sites as determined using capacitance‐frequency analysis. The resultingD^*of NIR–SWIR OPDs operating from 600–1400 nm under an applied bias of −2 V is improved by two orders of magnitude, from 10⁸to 10¹⁰ Jones (cm Hz^1/2 W⁻¹), when incorporating polysulfone within the blends. This broadly applicable strategy can reduce noise in IR‐OPDs enabling their practical operation and the realization of emerging technologies.

 

Emerging infrared photodetectors have reported a high level of gain using trap-assisted photomultiplication mechanisms enabling significant enhancements in their sensitivity. This work investigates a series of interfacial materials in order to understand how charge blocking layers facilitate trap-assisted photomultiplication in organic shortwave infrared detectors. The hole blocking layers induce accumulation of photogenerated holes at the interface, which in turn lowers the electron injection barrier and enables photomultiplication. In addition to examining photoresponse characteristics, the device dark current is analyzed by fitting to a charge injection model to quantify injection barriers. This demonstrates that the electric field induced barrier lowering effect plateaus with increasing applied bias. Among the interfaces studied, the best detectivity is observed using the hole blocking layer bathophenanthroline (Bphen), which reduces the probability of recombination and extends the lifetime of trapped holes to increase photomultiplication. This leads to a responsivity of 5.6 A W −1 (equivalent external quantum efficiency = 660% at 1050 nm) and detectivity of 10 9 Jones with broadband operation from 600 nm to 1400 nm.